US10246343B2 - Processing of cobaltous sulpha/dithionate liquors derived from cobalt resource - Google Patents
Processing of cobaltous sulpha/dithionate liquors derived from cobalt resource Download PDFInfo
- Publication number
- US10246343B2 US10246343B2 US15/806,183 US201715806183A US10246343B2 US 10246343 B2 US10246343 B2 US 10246343B2 US 201715806183 A US201715806183 A US 201715806183A US 10246343 B2 US10246343 B2 US 10246343B2
- Authority
- US
- United States
- Prior art keywords
- lithium
- sodium
- dithionate
- cobalt
- liquor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Co2O3+SO2+H2SO4=2CoSO4+H2O
Co2O3+2SO2+H2SO4=2CoS2O6+H2O
2LiCoO2+SO2+2H2SO4═Li2SO4+2CoSO4+2H2O
2LiCoO2+3SO2+2H2SO4═Li2SO4+2CoS2O6+2H2O
2LiCoO2+4SO2+2H2SO4═Li2S2O6+2CoS2O6+2H2O
2LiNi0.33Mn0.33Co0.33O2+SO2+2H2SO4═Li2SO4+2(Ni,Co,Mn)SO4+2H2O
2LiNi0.33Mn0.33Co0.33O2+3SO2+2H2SO4═Li2SO4+2(Ni,Co,Mn)CoS2O6+2H2O
2LiNi0.33Mn0.33Co0.33O2+4SO2+2H2SO4═Li2S2O6+2(Ni,Co,Mn)S2O6+2H2O
2LiNi0.8Co0.15Al0.05O2+SO2+2H2SO4═Li2SO4+2(Ni,Co,Al)SO4+2H2O
2LiNi0.8Co0.15Al0.05O2+3SO2+2H2SO4═Li2SO4+2(Ni,Co,Al)CoS2O6+2H2O
2LiNi0.8Co0.15Al0.05O2+4SO2+2H2SO4═Li2S2O6+2(Ni,Co,Al)S2O6+2H2O
CoSO4+Na2CO3═CoCO3+Na2SO4 Near Complete Conversion
CoS2O6+Na2CO3═CoCO3+Na2S2O6 Near Complete Conversion
Li2SO4+Na2CO3═Li2CO3+Na2SO4 Partial Conversion
Li2S2O6+Na2CO3═Li2CO3+Na2S2O6 Partial Conversion
(Ni,Mn,Co)SO4+Na2CO3═(Ni,Mn,Co)CO3+Na2SO4 Near Complete Conversion
(Ni,Mn,Co)S2O6+Na2CO3═(Ni,Mn,Co)CO3+Na2S2O6 Near Complete Conversion
Li2SO4+Na2CO3═Li2CO3+Na2SO4 Partial Conversion
Li2S2O6+Na2CO3═Li2CO3+Na2S2O6 Partial Conversion
(Ni,Co,Al)SO4+Na2CO3═(Ni,Co,Al)CO3+Na2SO4 Near Complete Conversion
(Ni,Co,Al)S2O6+Na2CO3═(Ni,Co,Al)CO3+Na2S2O6 Near Complete Conversion
Li2SO4+Na2CO3═Li2CO3+Na2SO4 Partial Conversion
Li2S2O6+Na2CO3═Li2CO3+Na2S2O6 Partial Conversion
CoSO4+2NaOH═Co(OH)2+Na2SO4 Near Complete Conversion
CoS2O6+2NaOH═Co(OH)2+Na2S2O6 Near Complete Conversion
(Ni,Mn,Co)SO4+2NaOH═(Ni,Mn,Co)(OH)2+Na2SO4 Near Complete Conversion
(Ni,Mn,Co)S2O6+2NaOH═(Ni,Mn,Co)(OH)2+Na2S2O6 Near Complete Conversion
(Ni,Co,Al)SO4+2NaOH═(Ni,Co,Al)(OH)2+Na2SO4 Near Complete Conversion
(Ni,Co,Al)S2O6+2NaOH═(Ni,Co,Al)(OH)2+Na2S2O6 Near Complete Conversion
CoSO4+2LiOH═Co(OH)2+Li2SO4 Near Complete Conversion
CoS2O6+2LiOH═Co(OH)2+Li2S2O6 Near Complete Conversion
(Ni,Mn,Co)SO4+2LiOH═(Ni,Mn,Co)(OH)2+Li2SO4 Near Complete Conversion
(Ni,Mn,Co)S2O6+2LiOH═(Ni,Mn,Co)(OH)2+Li2S2O6 Near Complete Conversion
(Ni,Co,Al)SO4+2LiOH═(Ni,Co,Al)(OH)2+Li2SO4 Near Complete Conversion
(Ni,Co,Al)S2O6+2LiOH═(Ni,Co,Al)(OH)2+Li2S2O6 Near Complete Conversion
TABLE 1 | |||
Test Number | S2O6 2− (mg/L) | ||
| 27150 | ||
LT 19 | 30294 | ||
| 15207 | ||
LT 21 | 23069 | ||
| 13290 | ||
LT 23 | 30953 | ||
| 19951 | ||
LT 25 | 9260 | ||
| 10386 | ||
7. Locked Cycling Testing for Treating Lithium Cobalt Oxide
TABLE 2 | |||
Lock Cycle No. | | ||
1 | 32% | ||
2 | 36% | ||
3 | 68% | ||
4 | 76% | ||
Filtrate from the previous step containing a mixture of sodium sulphate, sodium dithionate and un-recovered lithium ion solution is cooled to 5° C. to for 2 hours with gentle mixing with an overhead mixer to crystallize sodium sulphate decahydrate and sodium dithionate dihydrate. The crystals were collected by filtration and dried as 60° C. to collect anhydrous crystals. The weight of the dry crystals for
TABLE 3 | |||
Weight of Dry | |||
Lock Cycle No. | Crystals (g) | ||
1 | 26.16 | ||
2 | 59.77 | ||
3 | 78.50 | ||
4 | 74.25 | ||
An Example of a nanofiltration step is described in Example 20.
8. Lithium Nickel Manganese Cobalt Oxide Leached with Sulphur Dioxide and Sulphuric Acid (Test #NMC3-5)
TABLE 4 | |||
Lock Cycle No. | | ||
1 | 47% | ||
2 | 67% | ||
3 | 78% | ||
4 | 100% | ||
Filtrate from the previous step containing a mixture of sodium sulphate, sodium dithionate and un-recovered lithium ion solution was cooled to 5° C. to for 2 hours with gentle mixing using an overhead mixer to crystallize sodium sulphate decahydrate and sodium dithionate dihydrate. The crystals were collected by filtration and dried as 60° C. to collect anhydrous crystals. The weights of the dry crystals for
TABLE 5 | |||
Weight of Dry | |||
Lock Cycle No. | Crystals (g) | ||
1 | 53.22 | ||
2 | 108.29 | ||
3 | 71.75 | ||
4 | 236.11 | ||
An Example of a nanofiltration step is described in Example 20.
14. Lithium Nickel Cobalt Aluminum Oxide Leached with Sulphur Dioxide and Sulphuric Acid (Test #NCA-LT8)
TABLE 6 | |||
Lock Cycle No. | |
||
1 | 51% | ||
2 | 62% | ||
3 | 69% | ||
4 | 70% | ||
5 | 80% | ||
6 | 86% | ||
7 | 100% | ||
TABLE 7 | |||
Weight of Dry | |||
Lock Cycle No. | Crystals (g) | ||
1 | 67.9 | ||
2 | 185.3 | ||
3 | 161.4 | ||
4 | 175.0 | ||
5 | 218.7 | ||
6 | 109.3 | ||
7 | 205.6 | ||
An Example of a nanofiltration step is described in Example 20.
20. Nanofiltration
Claims (50)